Huntsman IROGRAN ®A85E4607 Thermoplastic Polyurethane Technical Data Sheet
|
Huntsman IROGRAN A85E4607主要应用于密封圈，厚壁技术部件如同步带，休闲鞋底，挤出厚壁型材，螺旋管和输送软管。
|
Physical Properties物性
|
测试标准
|
数值
|
单位
|
Density密度
|
ISO 1183-1
|
1.19
|
kg/m³
|
Melt Volume Rate(190°C/21,6kg)
|
ISO 1133-1
|
35
|
cm³/10min
|
Hardness硬度
|
ISO 7619
|
85±2
|
Shore A
|
Hardness硬度
|
ISO 7619
|
34±2
|
Shore D
|
Mold Shrinkage收缩率
|
ISO 294-4
|
1.0
|
%
|
Tensile strength抗拉强度
|
DIN53504
|
45
|
MPa
|
Elongation at Break断裂伸长率
|
DIN53504
|
650
|
%
|
50%Modulus伸长模量
|
DIN53504
|
4.27
|
MPa
|
100%Modulus伸长模量
|
DIN53504
|
5.0
|
MPa
|
300%Modulus伸长模量
|
DIN53504
|
14
|
MPa
|
Tear strength撕裂强度
|
ISO 34-1
|
70
|
KN/m
|
Flexural modulus @ 23℃弯曲模量
|
ASTM D 790
|
24
|
MPa
|
Flexural modulus @ -29℃弯曲模量
|
ASTM D 790
|
60
|
MPa
|
Bayshore rebound resilience回弹性
|
ASTM D 2632
|
50
|
%
|
Compression Set压缩变形率23℃×22h
|
ASTM D-395
|
25
|
%
|
Compression Set压缩变形率23℃×70h
|
ASTM D-395
|
35
|
%
|
Compression Set压缩变形率70℃×24h
|
ASTM D-395
|
43
|
%
|
Abrasion耐磨性
|
ISO 4649
|
25
|
mm³
|
Softening range low软化温度(低点)
|
Huntsman TMA
|
160
|
℃
|
Softening range high软化温度(高点)
|
Huntsman TMA
|
185
|
℃
|
Vicat Softening Point维卡软化温度
|
ASTM D 1525
|
83
|
℃
|
Glass transition temperature(DSC)玻璃化转变温度
|
ASTM D 3418
|
-41
|
℃
|
Dew Point露点
|
|
-30
|
℃
|
Melt Range熔融温度范围
|
|
165~200
|
℃
|
Mold Temperature模具温度
|
|
20~40
|
℃
|